Cordierite vs. Low Expansion Glass-ceramic
Cordierite belongs to the oxide-based engineering ceramics classification, while low expansion glass-ceramic belongs to the glass and glass-ceramics. There are 16 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is cordierite and the bottom bar is low expansion glass-ceramic.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 62 | |
| 83 |
| Flexural Strength, MPa | 17 to 32 | |
| 35 |
| Tensile Strength: Ultimate (UTS), MPa | 190 | |
| 53 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 1150 | |
| 690 |
| Specific Heat Capacity, J/kg-K | 800 to 850 | |
| 800 |
| Thermal Conductivity, W/m-K | 1.3 to 1.7 | |
| 1.5 |
| Thermal Expansion, µm/m-K | 2.9 to 4.8 | |
| 1.7 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 MHz | 4.7 | |
| 5.7 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 9.5 | |
| 11 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.0 to 2.2 | |
| 2.4 |
Common Calculations
| Stiffness to Weight: Axial, points | 15 to 17 | |
| 19 |
| Stiffness to Weight: Bending, points | 59 to 67 | |
| 59 |
| Strength to Weight: Axial, points | 24 to 27 | |
| 6.1 |
| Strength to Weight: Bending, points | 33 to 38 | |
| 13 |
| Thermal Diffusivity, mm2/s | 0.74 to 1.0 | |
| 0.76 |
| Thermal Shock Resistance, points | 47 to 78 | |
| 28 |