Cordierite vs. Magnesium Titanate
Both cordierite and magnesium titanate are oxide-based engineering ceramics. There are 8 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is cordierite and the bottom bar is magnesium titanate.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 2.0 to 2.2 | |
| 3.5 |
| Dielectric Strength (Breakdown Potential), kV/mm | 7.7 | |
| 9.1 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 9.5 | |
| 9.0 |
| Flexural Strength, MPa | 17 to 32 | |
| 80 |
| Specific Heat Capacity, J/kg-K | 800 to 850 | |
| 950 |
| Thermal Conductivity, W/m-K | 1.3 to 1.7 | |
| 3.8 |
| Thermal Diffusivity, mm2/s | 0.74 to 1.0 | |
| 1.1 |
| Thermal Expansion, µm/m-K | 2.9 to 4.8 | |
| 8.0 |