EN 1.7106 +CH Steel vs. EN 1.7701 +CH Steel
Both EN 1.7106 +CH steel and EN 1.7701 +CH steel are iron alloys. Both are furnished in the core hardened (CH) condition. They have a very high 98% of their average alloy composition in common.
For each property being compared, the top bar is EN 1.7106 +CH steel and the bottom bar is EN 1.7701 +CH steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Rockwell C Hardness | 54 | |
| 52 |
| Shear Modulus, GPa | 72 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 1750 | |
| 1680 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 410 | |
| 420 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1460 |
| Melting Onset (Solidus), °C | 1390 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 46 | |
| 44 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.4 | |
| 7.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.6 | |
| 8.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.1 | |
| 2.6 |
| Density, g/cm3 | 7.7 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 1.9 |
| Embodied Energy, MJ/kg | 20 | |
| 26 |
| Embodied Water, L/kg | 47 | |
| 52 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 63 | |
| 60 |
| Strength to Weight: Bending, points | 42 | |
| 40 |
| Thermal Diffusivity, mm2/s | 13 | |
| 12 |
| Thermal Shock Resistance, points | 53 | |
| 50 |
Alloy Composition
| Carbon (C), % | 0.52 to 0.6 | |
| 0.48 to 0.56 |
| Chromium (Cr), % | 0.2 to 0.45 | |
| 0.9 to 1.2 |
| Iron (Fe), % | 95.9 to 97 | |
| 96.2 to 97.7 |
| Manganese (Mn), % | 0.7 to 1.0 | |
| 0.7 to 1.1 |
| Molybdenum (Mo), % | 0 | |
| 0.15 to 0.3 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.025 |
| Silicon (Si), % | 1.6 to 2.0 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.025 |
| Vanadium (V), % | 0 | |
| 0.1 to 0.2 |