DAP vs. PS
DAP belongs to the thermoset plastics classification, while PS belongs to the thermoplastics. There are 18 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is DAP and the bottom bar is PS.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 13 | |
| 1.9 to 2.9 |
| Elongation at Break, % | 31 | |
| 1.8 to 40 |
| Flexural Strength, MPa | 62 | |
| 62 to 80 |
| Impact Strength: Notched Izod, J/m | 14 | |
| 19 to 45 |
| Tensile Strength: Ultimate (UTS), MPa | 28 | |
| 32 to 44 |
Thermal Properties
| Glass Transition Temperature, °C | 150 | |
| 100 |
| Specific Heat Capacity, J/kg-K | 1450 | |
| 1250 to 1400 |
| Thermal Conductivity, W/m-K | 0.6 | |
| 0.14 to 0.22 |
| Thermal Expansion, µm/m-K | 25 | |
| 80 to 98 |
Electrical Properties
| Dielectric Strength (Breakdown Potential), kV/mm | 40 | |
| 18 to 20 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 13 | |
| 14 to 15 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.7 | |
| 1.0 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.1 | |
| 1.0 to 1.5 |
| Stiffness to Weight: Bending, points | 46 | |
| 40 to 45 |
| Strength to Weight: Axial, points | 4.5 | |
| 8.5 to 12 |
| Strength to Weight: Bending, points | 12 | |
| 22 to 26 |
| Thermal Diffusivity, mm2/s | 0.24 | |
| 0.11 to 0.15 |
| Thermal Shock Resistance, points | 6.3 | |
| 11 to 15 |