DAP vs. Thermoset PI
Both DAP and thermoset PI are thermoset plastics. There are 16 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is DAP and the bottom bar is thermoset PI.
Metric UnitsUS Customary Units
Mechanical Properties
| Compressive (Crushing) Strength, MPa | 150 | |
| 120 to 210 |
| Elongation at Break, % | 31 | |
| 2.0 to 5.9 |
| Flexural Strength, MPa | 62 | |
| 60 to 100 |
| Impact Strength: Notched Izod, J/m | 14 | |
| 21 to 43 |
| Tensile Strength: Ultimate (UTS), MPa | 28 | |
| 37 to 81 |
Thermal Properties
| Glass Transition Temperature, °C | 150 | |
| 360 |
| Heat Deflection Temperature At 1.82 MPa (264 psi), °C | 160 | |
| 370 |
| Specific Heat Capacity, J/kg-K | 1450 | |
| 1130 |
| Thermal Conductivity, W/m-K | 0.6 | |
| 0.29 to 1.7 |
| Thermal Expansion, µm/m-K | 25 | |
| 38 to 54 |
Electrical Properties
| Dielectric Strength (Breakdown Potential), kV/mm | 40 | |
| 20 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 13 | |
| 15 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.7 | |
| 1.4 to 1.6 |
Common Calculations
| Strength to Weight: Axial, points | 4.5 | |
| 6.5 to 16 |
| Strength to Weight: Bending, points | 12 | |
| 16 to 30 |
| Thermal Diffusivity, mm2/s | 0.24 | |
| 0.18 to 0.95 |