R31539 Cobalt vs. C71640 Copper-nickel
R31539 cobalt belongs to the cobalt alloys classification, while C71640 copper-nickel belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is R31539 cobalt and the bottom bar is C71640 copper-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 140 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 86 | |
| 52 |
| Tensile Strength: Ultimate (UTS), MPa | 1000 to 1340 | |
| 490 to 630 |
| Tensile Strength: Yield (Proof), MPa | 590 to 940 | |
| 190 to 460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 240 |
| Melting Completion (Liquidus), °C | 1360 | |
| 1180 |
| Melting Onset (Solidus), °C | 1290 | |
| 1120 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 410 |
| Thermal Conductivity, W/m-K | 13 | |
| 29 |
| Thermal Expansion, µm/m-K | 13 | |
| 15 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.0 | |
| 7.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.1 | |
| 7.1 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.4 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 8.2 | |
| 5.0 |
| Embodied Energy, MJ/kg | 110 | |
| 73 |
| Embodied Water, L/kg | 530 | |
| 280 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 780 to 2000 | |
| 130 to 750 |
| Stiffness to Weight: Axial, points | 15 | |
| 8.7 |
| Stiffness to Weight: Bending, points | 24 | |
| 20 |
| Strength to Weight: Axial, points | 33 to 44 | |
| 15 to 20 |
| Strength to Weight: Bending, points | 27 to 32 | |
| 16 to 18 |
| Thermal Diffusivity, mm2/s | 3.5 | |
| 8.2 |
| Thermal Shock Resistance, points | 24 to 32 | |
| 16 to 21 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0.3 to 1.0 | |
| 0 |
| Carbon (C), % | 0 to 0.14 | |
| 0 |
| Chromium (Cr), % | 26 to 30 | |
| 0 |
| Cobalt (Co), % | 57.7 to 68.7 | |
| 0 |
| Copper (Cu), % | 0 | |
| 61.7 to 67.8 |
| Iron (Fe), % | 0 to 0.75 | |
| 1.7 to 2.3 |
| Lanthanum (La), % | 0.030 to 0.2 | |
| 0 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 to 1.0 | |
| 1.5 to 2.5 |
| Molybdenum (Mo), % | 5.0 to 7.0 | |
| 0 |
| Nickel (Ni), % | 0 to 1.0 | |
| 29 to 32 |
| Nitrogen (N), % | 0 to 0.25 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 1.0 |
| Residuals, % | 0 | |
| 0 to 0.5 |