Ductile Hardened ASTM B540 vs. Work Hardened 88-silver 12-tin-oxide
Both ductile hardened ASTM B540 and work hardened 88-silver 12-tin-oxide are otherwise unclassified metals. Both are furnished in the cold worked (strain hardened) condition. There are 6 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.
For each property being compared, the top bar is ductile hardened ASTM B540 and the bottom bar is work hardened 88-silver 12-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 5.5 | |
| 84 |
| Elongation at Break, % | 9.1 | |
| 9.0 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 99 | |
| 24 |
| Shear Strength, MPa | 690 | |
| 160 |
| Tensile Strength: Ultimate (UTS), MPa | 1170 | |
| 280 |
| Tensile Strength: Yield (Proof), MPa | 930 | |
| 260 |