EN 1.0031 Steel vs. ACI-ASTM CA15M Steel

Both EN 1.0031 steel and ACI-ASTM CA15M steel are iron alloys. They have 86% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.0031 steel and the bottom bar is ACI-ASTM CA15M steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 89
210
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 28
20
Fatigue Strength, MPa 160
330
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Tensile Strength: Ultimate (UTS), MPa 310
690
Tensile Strength: Yield (Proof), MPa 210
510

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Maximum Temperature: Mechanical, °C 400
760
Melting Completion (Liquidus), °C 1470
1450
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 53
27
Thermal Expansion, µm/m-K 12
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
3.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
3.5

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
7.5
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.4
2.1
Embodied Energy, MJ/kg 18
29
Embodied Water, L/kg 45
100

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 78
130
Resilience: Unit (Modulus of Resilience), kJ/m3 120
670
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 11
25
Strength to Weight: Bending, points 13
22
Thermal Diffusivity, mm2/s 14
7.2
Thermal Shock Resistance, points 9.8
25

Alloy Composition

Carbon (C), % 0 to 0.1
0 to 0.15
Chromium (Cr), % 0
11.5 to 14
Iron (Fe), % 98.8 to 100
82.1 to 88.4
Manganese (Mn), % 0 to 0.7
0 to 1.0
Molybdenum (Mo), % 0
0.15 to 1.0
Nickel (Ni), % 0
0 to 1.0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 0.35
0 to 0.65
Sulfur (S), % 0 to 0.045
0 to 0.040