EN 1.0031 Steel vs. ASTM A372 Grade K Steel

Both EN 1.0031 steel and ASTM A372 grade K steel are iron alloys. They have a very high 95% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.0031 steel and the bottom bar is ASTM A372 grade K steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 89
230
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 28
23
Fatigue Strength, MPa 160
440
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 200
490
Tensile Strength: Ultimate (UTS), MPa 310
780
Tensile Strength: Yield (Proof), MPa 210
620

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
440
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 53
48
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
7.8
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
4.4
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 1.4
1.8
Embodied Energy, MJ/kg 18
24
Embodied Water, L/kg 45
57

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 78
160
Resilience: Unit (Modulus of Resilience), kJ/m3 120
1010
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 11
27
Strength to Weight: Bending, points 13
24
Thermal Diffusivity, mm2/s 14
13
Thermal Shock Resistance, points 9.8
23

Alloy Composition

Carbon (C), % 0 to 0.1
0 to 0.18
Chromium (Cr), % 0
1.0 to 1.8
Iron (Fe), % 98.8 to 100
93.4 to 96.6
Manganese (Mn), % 0 to 0.7
0.1 to 0.4
Molybdenum (Mo), % 0
0.2 to 0.6
Nickel (Ni), % 0
2.0 to 3.3
Phosphorus (P), % 0 to 0.045
0 to 0.015
Silicon (Si), % 0 to 0.35
0.15 to 0.35
Sulfur (S), % 0 to 0.045
0 to 0.010