EN 1.0031 Steel vs. EN 1.4411 Stainless Steel

Both EN 1.0031 steel and EN 1.4411 stainless steel are iron alloys. They have 77% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.0031 steel and the bottom bar is EN 1.4411 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 28
17
Fatigue Strength, MPa 160
370
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
78
Tensile Strength: Ultimate (UTS), MPa 310
870
Tensile Strength: Yield (Proof), MPa 210
600

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 400
880
Melting Completion (Liquidus), °C 1470
1450
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 53
17
Thermal Expansion, µm/m-K 12
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
13
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.4
3.0
Embodied Energy, MJ/kg 18
41
Embodied Water, L/kg 45
130

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 78
130
Resilience: Unit (Modulus of Resilience), kJ/m3 120
920
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 11
31
Strength to Weight: Bending, points 13
26
Thermal Diffusivity, mm2/s 14
4.6
Thermal Shock Resistance, points 9.8
28

Alloy Composition

Carbon (C), % 0 to 0.1
0 to 0.060
Chromium (Cr), % 0
15 to 17
Iron (Fe), % 98.8 to 100
73.1 to 79.5
Manganese (Mn), % 0 to 0.7
0 to 1.0
Molybdenum (Mo), % 0
1.5 to 2.0
Nickel (Ni), % 0
4.0 to 6.0
Phosphorus (P), % 0 to 0.045
0 to 0.035
Silicon (Si), % 0 to 0.35
0 to 0.8
Sulfur (S), % 0 to 0.045
0 to 0.025