EN 1.0031 Steel vs. EN 1.4530 Stainless Steel

Both EN 1.0031 steel and EN 1.4530 stainless steel are iron alloys. They have 76% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is EN 1.0031 steel and the bottom bar is EN 1.4530 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Tensile Strength: Ultimate (UTS), MPa 310
1030 to 1370

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Maximum Temperature: Mechanical, °C 400
790
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Expansion, µm/m-K 12
11

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
15
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 1.4
3.4
Embodied Energy, MJ/kg 18
46
Embodied Water, L/kg 45
130

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 11
36 to 48
Strength to Weight: Bending, points 13
29 to 35
Thermal Shock Resistance, points 9.8
35 to 47

Alloy Composition

Aluminum (Al), % 0
0.6 to 0.8
Carbon (C), % 0 to 0.1
0 to 0.015
Chromium (Cr), % 0
11.5 to 12.5
Iron (Fe), % 98.8 to 100
74.4 to 77.3
Manganese (Mn), % 0 to 0.7
0 to 0.1
Molybdenum (Mo), % 0
1.9 to 2.2
Nickel (Ni), % 0
8.5 to 9.5
Nitrogen (N), % 0
0 to 0.010
Phosphorus (P), % 0 to 0.045
0 to 0.010
Silicon (Si), % 0 to 0.35
0 to 0.1
Sulfur (S), % 0 to 0.045
0 to 0.0050
Titanium (Ti), % 0
0.28 to 0.37