EN 1.0031 Steel vs. EN 1.4571 Stainless Steel

Both EN 1.0031 steel and EN 1.4571 stainless steel are iron alloys. They have 67% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.0031 steel and the bottom bar is EN 1.4571 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 89
190 to 270
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 28
14 to 40
Fatigue Strength, MPa 160
200 to 330
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
78
Shear Strength, MPa 200
410 to 550
Tensile Strength: Ultimate (UTS), MPa 310
600 to 900
Tensile Strength: Yield (Proof), MPa 210
230 to 570

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 400
950
Melting Completion (Liquidus), °C 1470
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 53
15
Thermal Expansion, µm/m-K 12
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
19
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 1.4
3.9
Embodied Energy, MJ/kg 18
54
Embodied Water, L/kg 45
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 78
110 to 190
Resilience: Unit (Modulus of Resilience), kJ/m3 120
130 to 820
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 11
21 to 32
Strength to Weight: Bending, points 13
20 to 26
Thermal Diffusivity, mm2/s 14
4.0
Thermal Shock Resistance, points 9.8
13 to 20

Alloy Composition

Carbon (C), % 0 to 0.1
0 to 0.080
Chromium (Cr), % 0
16.5 to 18.5
Iron (Fe), % 98.8 to 100
61.7 to 71
Manganese (Mn), % 0 to 0.7
0 to 2.0
Molybdenum (Mo), % 0
2.0 to 2.5
Nickel (Ni), % 0
10.5 to 13.5
Phosphorus (P), % 0 to 0.045
0 to 0.045
Silicon (Si), % 0 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.045
0 to 0.015
Titanium (Ti), % 0
0 to 0.7