EN 1.0031 Steel vs. SAE-AISI 1213 Steel

Both EN 1.0031 steel and SAE-AISI 1213 steel are iron alloys. Their average alloy composition is basically identical. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.0031 steel and the bottom bar is SAE-AISI 1213 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 89
140 to 190
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 28
11 to 29
Fatigue Strength, MPa 160
200 to 290
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 200
290 to 360
Tensile Strength: Ultimate (UTS), MPa 310
440 to 600
Tensile Strength: Yield (Proof), MPa 210
260 to 470

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 53
51
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
1.8
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 18
18
Embodied Water, L/kg 45
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 78
63 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 120
180 to 580
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 11
16 to 21
Strength to Weight: Bending, points 13
17 to 20
Thermal Diffusivity, mm2/s 14
14
Thermal Shock Resistance, points 9.8
14 to 19

Alloy Composition

Carbon (C), % 0 to 0.1
0 to 0.13
Iron (Fe), % 98.8 to 100
98.4 to 99
Manganese (Mn), % 0 to 0.7
0.7 to 1.0
Phosphorus (P), % 0 to 0.045
0.070 to 0.12
Silicon (Si), % 0 to 0.35
0
Sulfur (S), % 0 to 0.045
0.24 to 0.33