EN 1.0031 Steel vs. SAE-AISI 4419 Steel

Both EN 1.0031 steel and SAE-AISI 4419 steel are iron alloys. Their average alloy composition is basically identical.

For each property being compared, the top bar is EN 1.0031 steel and the bottom bar is SAE-AISI 4419 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 89
150
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 28
23
Fatigue Strength, MPa 160
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 200
310
Tensile Strength: Ultimate (UTS), MPa 310
490
Tensile Strength: Yield (Proof), MPa 210
270

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
410
Melting Completion (Liquidus), °C 1470
1470
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 53
50
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
2.4
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 1.4
1.5
Embodied Energy, MJ/kg 18
20
Embodied Water, L/kg 45
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 78
97
Resilience: Unit (Modulus of Resilience), kJ/m3 120
190
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 11
17
Strength to Weight: Bending, points 13
18
Thermal Diffusivity, mm2/s 14
13
Thermal Shock Resistance, points 9.8
14

Alloy Composition

Carbon (C), % 0 to 0.1
0.18 to 0.23
Iron (Fe), % 98.8 to 100
98.1 to 98.8
Manganese (Mn), % 0 to 0.7
0.45 to 0.65
Molybdenum (Mo), % 0
0.45 to 0.6
Phosphorus (P), % 0 to 0.045
0 to 0.035
Silicon (Si), % 0 to 0.35
0.15 to 0.35
Sulfur (S), % 0 to 0.045
0 to 0.040