EN 1.0031 Steel vs. SAE-AISI 94B30 Steel

Both EN 1.0031 steel and SAE-AISI 94B30 steel are iron alloys. They have a very high 98% of their average alloy composition in common.

For each property being compared, the top bar is EN 1.0031 steel and the bottom bar is SAE-AISI 94B30 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 89
150
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 28
25
Fatigue Strength, MPa 160
220
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 200
320
Tensile Strength: Ultimate (UTS), MPa 310
500
Tensile Strength: Yield (Proof), MPa 210
300

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
410
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 53
39
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
2.4
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.5
Embodied Energy, MJ/kg 18
20
Embodied Water, L/kg 45
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 78
110
Resilience: Unit (Modulus of Resilience), kJ/m3 120
250
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 11
18
Strength to Weight: Bending, points 13
18
Thermal Diffusivity, mm2/s 14
10
Thermal Shock Resistance, points 9.8
15

Alloy Composition

Boron (B), % 0
0.00050 to 0.0030
Carbon (C), % 0 to 0.1
0.28 to 0.33
Chromium (Cr), % 0
0.3 to 0.5
Iron (Fe), % 98.8 to 100
97 to 98.1
Manganese (Mn), % 0 to 0.7
0.75 to 1.0
Molybdenum (Mo), % 0
0.080 to 0.15
Nickel (Ni), % 0
0.3 to 0.6
Phosphorus (P), % 0 to 0.045
0 to 0.035
Silicon (Si), % 0 to 0.35
0.15 to 0.35
Sulfur (S), % 0 to 0.045
0 to 0.040