EN 1.0031 Steel vs. S17700 Stainless Steel

Both EN 1.0031 steel and S17700 stainless steel are iron alloys. They have 74% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.0031 steel and the bottom bar is S17700 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 89
180 to 430
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 28
1.0 to 23
Fatigue Strength, MPa 160
290 to 560
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Shear Strength, MPa 200
740 to 940
Tensile Strength: Ultimate (UTS), MPa 310
1180 to 1650
Tensile Strength: Yield (Proof), MPa 210
430 to 1210

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 400
890
Melting Completion (Liquidus), °C 1470
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 53
15
Thermal Expansion, µm/m-K 12
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
13
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 1.4
2.8
Embodied Energy, MJ/kg 18
40
Embodied Water, L/kg 45
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 78
15 to 210
Resilience: Unit (Modulus of Resilience), kJ/m3 120
460 to 3750
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 11
42 to 59
Strength to Weight: Bending, points 13
32 to 40
Thermal Diffusivity, mm2/s 14
4.1
Thermal Shock Resistance, points 9.8
39 to 54

Alloy Composition

Aluminum (Al), % 0
0.75 to 1.5
Carbon (C), % 0 to 0.1
0 to 0.090
Chromium (Cr), % 0
16 to 18
Iron (Fe), % 98.8 to 100
70.5 to 76.8
Manganese (Mn), % 0 to 0.7
0 to 1.0
Nickel (Ni), % 0
6.5 to 7.8
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.045
0 to 0.030