EN 1.0031 Steel vs. S66286 Stainless Steel

Both EN 1.0031 steel and S66286 stainless steel are iron alloys. They have 55% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.0031 steel and the bottom bar is S66286 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 28
17 to 40
Fatigue Strength, MPa 160
240 to 410
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
75
Shear Strength, MPa 200
420 to 630
Tensile Strength: Ultimate (UTS), MPa 310
620 to 1020
Tensile Strength: Yield (Proof), MPa 210
280 to 670

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 400
920
Melting Completion (Liquidus), °C 1470
1430
Melting Onset (Solidus), °C 1420
1370
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 53
15
Thermal Expansion, µm/m-K 12
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
1.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
2.2

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
26
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 1.4
6.0
Embodied Energy, MJ/kg 18
87
Embodied Water, L/kg 45
170

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 78
150 to 200
Resilience: Unit (Modulus of Resilience), kJ/m3 120
190 to 1150
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 11
22 to 36
Strength to Weight: Bending, points 13
20 to 28
Thermal Diffusivity, mm2/s 14
4.0
Thermal Shock Resistance, points 9.8
13 to 22

Alloy Composition

Aluminum (Al), % 0
0 to 0.35
Boron (B), % 0
0.0010 to 0.010
Carbon (C), % 0 to 0.1
0 to 0.080
Chromium (Cr), % 0
13.5 to 16
Iron (Fe), % 98.8 to 100
49.1 to 59.5
Manganese (Mn), % 0 to 0.7
0 to 2.0
Molybdenum (Mo), % 0
1.0 to 1.5
Nickel (Ni), % 0
24 to 27
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.045
0 to 0.030
Titanium (Ti), % 0
1.9 to 2.4
Vanadium (V), % 0
0.1 to 0.5