EN 1.0033 Steel vs. SAE-AISI 1017 Steel

Both EN 1.0033 steel and SAE-AISI 1017 steel are iron alloys. Their average alloy composition is basically identical. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.0033 steel and the bottom bar is SAE-AISI 1017 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 86 to 96
120 to 130
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 17 to 32
20 to 30
Fatigue Strength, MPa 120 to 140
170 to 270
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 200
280 to 290
Tensile Strength: Ultimate (UTS), MPa 300 to 330
420 to 460
Tensile Strength: Yield (Proof), MPa 150 to 200
220 to 390

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1470
1470
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 53
53
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
6.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
7.9

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
1.8
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 18
18
Embodied Water, L/kg 45
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 48 to 83
88 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 63 to 100
130 to 400
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 10 to 12
15 to 16
Strength to Weight: Bending, points 13 to 14
16 to 17
Thermal Diffusivity, mm2/s 14
14
Thermal Shock Resistance, points 9.4 to 10
13 to 14

Alloy Composition

Carbon (C), % 0 to 0.11
0.15 to 0.2
Iron (Fe), % 98.8 to 100
99.11 to 99.55
Manganese (Mn), % 0 to 0.7
0.3 to 0.6
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 0.35
0
Sulfur (S), % 0 to 0.045
0 to 0.050

Comparable Variants