EN 1.0033 Steel vs. R30816 Cobalt

EN 1.0033 steel belongs to the iron alloys classification, while R30816 cobalt belongs to the cobalt alloys. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.0033 steel and the bottom bar is R30816 cobalt.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 86 to 96
280
Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 17 to 32
23
Fatigue Strength, MPa 120 to 140
250
Poisson's Ratio 0.29
0.3
Shear Modulus, GPa 73
81
Tensile Strength: Ultimate (UTS), MPa 300 to 330
1020
Tensile Strength: Yield (Proof), MPa 150 to 200
460

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Melting Completion (Liquidus), °C 1470
1540
Melting Onset (Solidus), °C 1420
1460
Specific Heat Capacity, J/kg-K 470
420
Thermal Conductivity, W/m-K 53
13
Thermal Expansion, µm/m-K 12
12

Otherwise Unclassified Properties

Density, g/cm3 7.9
9.1
Embodied Carbon, kg CO2/kg material 1.4
20
Embodied Energy, MJ/kg 18
320
Embodied Water, L/kg 45
440

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 48 to 83
190
Resilience: Unit (Modulus of Resilience), kJ/m3 63 to 100
510
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
22
Strength to Weight: Axial, points 10 to 12
31
Strength to Weight: Bending, points 13 to 14
25
Thermal Diffusivity, mm2/s 14
3.3
Thermal Shock Resistance, points 9.4 to 10
28

Alloy Composition

Carbon (C), % 0 to 0.11
0.32 to 0.42
Chromium (Cr), % 0
19 to 21
Cobalt (Co), % 0
40 to 49.8
Iron (Fe), % 98.8 to 100
0 to 5.0
Manganese (Mn), % 0 to 0.7
1.0 to 2.0
Molybdenum (Mo), % 0
3.5 to 4.5
Nickel (Ni), % 0
19 to 21
Niobium (Nb), % 0
3.5 to 4.5
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.045
0 to 0.030
Tantalum (Ta), % 0
3.5 to 4.5
Tungsten (W), % 0
3.5 to 4.5