EN 1.0050 Steel vs. ASTM A387 Grade 91 Class 2

Both EN 1.0050 steel and ASTM A387 grade 91 class 2 are iron alloys. They have 89% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.0050 steel and the bottom bar is ASTM A387 grade 91 class 2.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
200
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 18
20
Fatigue Strength, MPa 190
330
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
75
Shear Strength, MPa 330
420
Tensile Strength: Ultimate (UTS), MPa 530
670
Tensile Strength: Yield (Proof), MPa 280
470

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Maximum Temperature: Mechanical, °C 400
600
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 53
26
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.8
8.9
Electrical Conductivity: Equal Weight (Specific), % IACS 7.8
10

Otherwise Unclassified Properties

Base Metal Price, % relative 1.7
7.0
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.4
2.6
Embodied Energy, MJ/kg 18
37
Embodied Water, L/kg 45
88

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 81
120
Resilience: Unit (Modulus of Resilience), kJ/m3 210
580
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
24
Strength to Weight: Bending, points 18
22
Thermal Diffusivity, mm2/s 14
6.9
Thermal Shock Resistance, points 17
19

Alloy Composition

Aluminum (Al), % 0
0 to 0.020
Carbon (C), % 0
0.080 to 0.12
Chromium (Cr), % 0
8.0 to 9.5
Iron (Fe), % 99.876 to 100
87.3 to 90.3
Manganese (Mn), % 0
0.3 to 0.6
Molybdenum (Mo), % 0
0.85 to 1.1
Nickel (Ni), % 0
0 to 0.4
Niobium (Nb), % 0
0.060 to 0.1
Nitrogen (N), % 0 to 0.014
0.030 to 0.070
Phosphorus (P), % 0 to 0.055
0 to 0.020
Silicon (Si), % 0
0.2 to 0.5
Sulfur (S), % 0 to 0.055
0 to 0.010
Titanium (Ti), % 0
0 to 0.010
Vanadium (V), % 0
0.18 to 0.25
Zirconium (Zr), % 0
0 to 0.010