MakeItFrom.com
Menu (ESC)

EN 1.0050 Steel vs. EN 1.0455 Cast Steel

Both EN 1.0050 steel and EN 1.0455 cast steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.0050 steel and the bottom bar is EN 1.0455 cast steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 18
25
Fatigue Strength, MPa 190
200
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 530
530
Tensile Strength: Yield (Proof), MPa 280
270

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 53
52
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.8
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 7.8
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 1.7
1.8
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 18
18
Embodied Water, L/kg 45
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 81
110
Resilience: Unit (Modulus of Resilience), kJ/m3 210
190
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19
19
Strength to Weight: Bending, points 18
18
Thermal Diffusivity, mm2/s 14
14
Thermal Shock Resistance, points 17
17

Alloy Composition

Carbon (C), % 0
0 to 0.23
Iron (Fe), % 99.876 to 100
97.9 to 100
Manganese (Mn), % 0
0 to 1.2
Nitrogen (N), % 0 to 0.014
0
Phosphorus (P), % 0 to 0.055
0 to 0.030
Silicon (Si), % 0
0 to 0.6
Sulfur (S), % 0 to 0.055
0 to 0.025