MakeItFrom.com
Menu (ESC)

EN 1.0050 Steel vs. EN 1.4451 Stainless Steel

Both EN 1.0050 steel and EN 1.4451 stainless steel are iron alloys. They have 60% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.0050 steel and the bottom bar is EN 1.4451 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
220
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 18
25
Fatigue Strength, MPa 190
370
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
80
Tensile Strength: Ultimate (UTS), MPa 530
750
Tensile Strength: Yield (Proof), MPa 280
540

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 400
1100
Melting Completion (Liquidus), °C 1470
1430
Melting Onset (Solidus), °C 1430
1380
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 53
17
Thermal Expansion, µm/m-K 12
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.8
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 7.8
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 1.7
20
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.4
3.8
Embodied Energy, MJ/kg 18
53
Embodied Water, L/kg 45
190

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 81
170
Resilience: Unit (Modulus of Resilience), kJ/m3 210
710
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
27
Strength to Weight: Bending, points 18
23
Thermal Diffusivity, mm2/s 14
4.5
Thermal Shock Resistance, points 17
16

Alloy Composition

Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0
25 to 27
Copper (Cu), % 0
2.8 to 3.5
Iron (Fe), % 99.876 to 100
56.2 to 64.6
Manganese (Mn), % 0
0 to 1.5
Molybdenum (Mo), % 0
2.5 to 3.5
Nickel (Ni), % 0
5.0 to 7.0
Nitrogen (N), % 0 to 0.014
0.12 to 0.22
Phosphorus (P), % 0 to 0.055
0 to 0.035
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0 to 0.055
0 to 0.025