EN 1.0050 Steel vs. EN 1.4589 Stainless Steel

Both EN 1.0050 steel and EN 1.4589 stainless steel are iron alloys. They have 82% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.0050 steel and the bottom bar is EN 1.4589 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 18
17
Fatigue Strength, MPa 190
260
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Shear Strength, MPa 330
400
Tensile Strength: Ultimate (UTS), MPa 530
650
Tensile Strength: Yield (Proof), MPa 280
440

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 400
810
Melting Completion (Liquidus), °C 1470
1450
Melting Onset (Solidus), °C 1430
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 53
25
Thermal Expansion, µm/m-K 12
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.8
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 7.8
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 1.7
9.5
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.4
2.4
Embodied Energy, MJ/kg 18
34
Embodied Water, L/kg 45
110

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 81
96
Resilience: Unit (Modulus of Resilience), kJ/m3 210
490
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
23
Strength to Weight: Bending, points 18
22
Thermal Diffusivity, mm2/s 14
6.7
Thermal Shock Resistance, points 17
23

Alloy Composition

Carbon (C), % 0
0 to 0.080
Chromium (Cr), % 0
13.5 to 15.5
Iron (Fe), % 99.876 to 100
78.2 to 85
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
0.2 to 1.2
Nickel (Ni), % 0
1.0 to 2.5
Nitrogen (N), % 0 to 0.014
0
Phosphorus (P), % 0 to 0.055
0 to 0.040
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0 to 0.055
0 to 0.015
Titanium (Ti), % 0
0.3 to 0.5