EN 1.0050 Steel vs. EN 1.4826 Stainless Steel

Both EN 1.0050 steel and EN 1.4826 stainless steel are iron alloys. They have 65% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.0050 steel and the bottom bar is EN 1.4826 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
150
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 18
9.1
Fatigue Strength, MPa 190
140
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Tensile Strength: Ultimate (UTS), MPa 530
500
Tensile Strength: Yield (Proof), MPa 280
260

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Maximum Temperature: Mechanical, °C 400
950
Melting Completion (Liquidus), °C 1470
1400
Melting Onset (Solidus), °C 1430
1360
Specific Heat Capacity, J/kg-K 470
490
Thermal Conductivity, W/m-K 53
14
Thermal Expansion, µm/m-K 12
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.8
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 7.8
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 1.7
17
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 1.4
3.3
Embodied Energy, MJ/kg 18
47
Embodied Water, L/kg 45
160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 81
39
Resilience: Unit (Modulus of Resilience), kJ/m3 210
170
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
18
Strength to Weight: Bending, points 18
18
Thermal Diffusivity, mm2/s 14
3.7
Thermal Shock Resistance, points 17
11

Alloy Composition

Carbon (C), % 0
0.3 to 0.5
Chromium (Cr), % 0
21 to 23
Iron (Fe), % 99.876 to 100
60.4 to 68.7
Manganese (Mn), % 0
0 to 2.0
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 0
9.0 to 11
Nitrogen (N), % 0 to 0.014
0
Phosphorus (P), % 0 to 0.055
0 to 0.040
Silicon (Si), % 0
1.0 to 2.5
Sulfur (S), % 0 to 0.055
0 to 0.030