EN 1.0050 Steel vs. EN 1.7366 Steel

Both EN 1.0050 steel and EN 1.7366 steel are iron alloys. They have a moderately high 94% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.0050 steel and the bottom bar is EN 1.7366 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
140 to 210
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 18
17 to 19
Fatigue Strength, MPa 190
160 to 320
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
74
Shear Strength, MPa 330
290 to 440
Tensile Strength: Ultimate (UTS), MPa 530
460 to 710
Tensile Strength: Yield (Proof), MPa 280
230 to 480

Thermal Properties

Latent Heat of Fusion, J/g 250
260
Maximum Temperature: Mechanical, °C 400
510
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 53
40
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.8
8.1
Electrical Conductivity: Equal Weight (Specific), % IACS 7.8
9.3

Otherwise Unclassified Properties

Base Metal Price, % relative 1.7
4.3
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.7
Embodied Energy, MJ/kg 18
23
Embodied Water, L/kg 45
69

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 81
74 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 210
140 to 600
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
16 to 25
Strength to Weight: Bending, points 18
17 to 23
Thermal Diffusivity, mm2/s 14
11
Thermal Shock Resistance, points 17
13 to 20

Alloy Composition

Carbon (C), % 0
0 to 0.18
Chromium (Cr), % 0
4.0 to 6.0
Iron (Fe), % 99.876 to 100
91.9 to 95.3
Manganese (Mn), % 0
0.3 to 0.8
Molybdenum (Mo), % 0
0.45 to 0.65
Nitrogen (N), % 0 to 0.014
0
Phosphorus (P), % 0 to 0.055
0 to 0.025
Silicon (Si), % 0
0 to 0.4
Sulfur (S), % 0 to 0.055
0 to 0.015