EN 1.0050 Steel vs. S40920 Stainless Steel

Both EN 1.0050 steel and S40920 stainless steel are iron alloys. They have 87% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.0050 steel and the bottom bar is S40920 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
150
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 18
22
Fatigue Strength, MPa 190
130
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
75
Shear Strength, MPa 330
270
Tensile Strength: Ultimate (UTS), MPa 530
430
Tensile Strength: Yield (Proof), MPa 280
190

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Maximum Temperature: Mechanical, °C 400
710
Melting Completion (Liquidus), °C 1470
1450
Melting Onset (Solidus), °C 1430
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 53
26
Thermal Expansion, µm/m-K 12
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.8
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 7.8
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 1.7
6.5
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 1.4
2.0
Embodied Energy, MJ/kg 18
28
Embodied Water, L/kg 45
94

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 81
78
Resilience: Unit (Modulus of Resilience), kJ/m3 210
97
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
15
Strength to Weight: Bending, points 18
16
Thermal Diffusivity, mm2/s 14
6.9
Thermal Shock Resistance, points 17
15

Alloy Composition

Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0
10.5 to 11.7
Iron (Fe), % 99.876 to 100
85.1 to 89.4
Manganese (Mn), % 0
0 to 1.0
Nickel (Ni), % 0
0 to 0.5
Niobium (Nb), % 0
0 to 0.1
Nitrogen (N), % 0 to 0.014
0 to 0.030
Phosphorus (P), % 0 to 0.055
0 to 0.040
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0 to 0.055
0 to 0.020
Titanium (Ti), % 0
0.15 to 0.5