EN 1.0060 Steel vs. AISI 314 Stainless Steel

Both EN 1.0060 steel and AISI 314 stainless steel are iron alloys. They have 52% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.0060 steel and the bottom bar is AISI 314 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
180
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 13
45
Fatigue Strength, MPa 200
210
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
78
Shear Strength, MPa 380
410
Tensile Strength: Ultimate (UTS), MPa 630
590
Tensile Strength: Yield (Proof), MPa 310
230

Thermal Properties

Latent Heat of Fusion, J/g 250
330
Maximum Temperature: Mechanical, °C 400
1100
Melting Completion (Liquidus), °C 1470
1380
Melting Onset (Solidus), °C 1430
1340
Specific Heat Capacity, J/kg-K 470
490
Thermal Conductivity, W/m-K 53
15
Thermal Expansion, µm/m-K 12
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.8
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 7.8
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 1.7
25
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 1.4
4.3
Embodied Energy, MJ/kg 18
62
Embodied Water, L/kg 45
190

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 70
210
Resilience: Unit (Modulus of Resilience), kJ/m3 250
130
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 22
21
Strength to Weight: Bending, points 21
20
Thermal Diffusivity, mm2/s 14
3.9
Thermal Shock Resistance, points 20
14

Alloy Composition

Carbon (C), % 0
0 to 0.25
Chromium (Cr), % 0
23 to 26
Iron (Fe), % 99.876 to 100
46.7 to 56.5
Manganese (Mn), % 0
0 to 2.0
Nickel (Ni), % 0
19 to 22
Nitrogen (N), % 0 to 0.014
0
Phosphorus (P), % 0 to 0.055
0 to 0.045
Silicon (Si), % 0
1.5 to 3.0
Sulfur (S), % 0 to 0.055
0 to 0.030