EN 1.0060 Steel vs. ASTM A182 Grade F5

Both EN 1.0060 steel and ASTM A182 grade F5 are iron alloys. They have a moderately high 93% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.0060 steel and the bottom bar is ASTM A182 grade F5.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
180
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 13
22
Fatigue Strength, MPa 200
220
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
74
Shear Strength, MPa 380
340
Tensile Strength: Ultimate (UTS), MPa 630
540
Tensile Strength: Yield (Proof), MPa 310
310

Thermal Properties

Latent Heat of Fusion, J/g 250
260
Maximum Temperature: Mechanical, °C 400
510
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 53
40
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.8
8.1
Electrical Conductivity: Equal Weight (Specific), % IACS 7.8
9.4

Otherwise Unclassified Properties

Base Metal Price, % relative 1.7
4.5
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.8
Embodied Energy, MJ/kg 18
24
Embodied Water, L/kg 45
69

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 70
100
Resilience: Unit (Modulus of Resilience), kJ/m3 250
260
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 22
19
Strength to Weight: Bending, points 21
19
Thermal Diffusivity, mm2/s 14
11
Thermal Shock Resistance, points 20
15

Alloy Composition

Carbon (C), % 0
0 to 0.15
Chromium (Cr), % 0
4.0 to 6.0
Iron (Fe), % 99.876 to 100
91.5 to 95.3
Manganese (Mn), % 0
0.3 to 0.6
Molybdenum (Mo), % 0
0.44 to 0.65
Nickel (Ni), % 0
0 to 0.5
Nitrogen (N), % 0 to 0.014
0
Phosphorus (P), % 0 to 0.055
0 to 0.030
Silicon (Si), % 0
0 to 0.5
Sulfur (S), % 0 to 0.055
0 to 0.030