EN 1.0060 Steel vs. EN 1.4016 Stainless Steel

Both EN 1.0060 steel and EN 1.4016 stainless steel are iron alloys. They have 82% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.0060 steel and the bottom bar is EN 1.4016 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
170
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 13
22
Fatigue Strength, MPa 200
190
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Shear Strength, MPa 380
330
Tensile Strength: Ultimate (UTS), MPa 630
520
Tensile Strength: Yield (Proof), MPa 310
290

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 400
870
Melting Completion (Liquidus), °C 1470
1440
Melting Onset (Solidus), °C 1430
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 53
25
Thermal Expansion, µm/m-K 12
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.8
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 7.8
3.4

Otherwise Unclassified Properties

Base Metal Price, % relative 1.7
8.5
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 1.4
2.1
Embodied Energy, MJ/kg 18
29
Embodied Water, L/kg 45
120

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 70
95
Resilience: Unit (Modulus of Resilience), kJ/m3 250
210
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 22
19
Strength to Weight: Bending, points 21
19
Thermal Diffusivity, mm2/s 14
6.7
Thermal Shock Resistance, points 20
19

Alloy Composition

Carbon (C), % 0
0 to 0.080
Chromium (Cr), % 0
16 to 18
Iron (Fe), % 99.876 to 100
79.9 to 84
Manganese (Mn), % 0
0 to 1.0
Nitrogen (N), % 0 to 0.014
0
Phosphorus (P), % 0 to 0.055
0 to 0.040
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0 to 0.055
0 to 0.015