EN 1.0060 Steel vs. EN 1.4563 Stainless Steel

Both EN 1.0060 steel and EN 1.4563 stainless steel are iron alloys. They have a modest 36% of their average alloy composition in common, which, by itself, doesn't mean much. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.0060 steel and the bottom bar is EN 1.4563 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
200
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 13
40
Fatigue Strength, MPa 200
210
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
80
Shear Strength, MPa 380
420
Tensile Strength: Ultimate (UTS), MPa 630
620
Tensile Strength: Yield (Proof), MPa 310
250

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Maximum Temperature: Mechanical, °C 400
1100
Melting Completion (Liquidus), °C 1470
1420
Melting Onset (Solidus), °C 1430
1370
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 53
12
Thermal Expansion, µm/m-K 12
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.8
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 7.8
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 1.7
36
Density, g/cm3 7.9
8.1
Embodied Carbon, kg CO2/kg material 1.4
6.3
Embodied Energy, MJ/kg 18
87
Embodied Water, L/kg 45
240

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 70
200
Resilience: Unit (Modulus of Resilience), kJ/m3 250
150
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 22
21
Strength to Weight: Bending, points 21
20
Thermal Diffusivity, mm2/s 14
3.2
Thermal Shock Resistance, points 20
13

Alloy Composition

Carbon (C), % 0
0 to 0.020
Chromium (Cr), % 0
26 to 28
Copper (Cu), % 0
0.7 to 1.5
Iron (Fe), % 99.876 to 100
31.6 to 40.3
Manganese (Mn), % 0
0 to 2.0
Molybdenum (Mo), % 0
3.0 to 4.0
Nickel (Ni), % 0
30 to 32
Nitrogen (N), % 0 to 0.014
0 to 0.1
Phosphorus (P), % 0 to 0.055
0 to 0.030
Silicon (Si), % 0
0 to 0.7
Sulfur (S), % 0 to 0.055
0 to 0.010