EN 1.0060 Steel vs. SAE-AISI 1043 Steel

Both EN 1.0060 steel and SAE-AISI 1043 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.0060 steel and the bottom bar is SAE-AISI 1043 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
190 to 200
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 13
13 to 18
Fatigue Strength, MPa 200
230 to 390
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 380
400 to 430
Tensile Strength: Ultimate (UTS), MPa 630
650 to 710
Tensile Strength: Yield (Proof), MPa 310
350 to 600

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 53
51
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.8
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 7.8
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 1.7
1.8
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 18
18
Embodied Water, L/kg 45
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 70
87 to 100
Resilience: Unit (Modulus of Resilience), kJ/m3 250
320 to 980
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 22
23 to 25
Strength to Weight: Bending, points 21
21 to 22
Thermal Diffusivity, mm2/s 14
14
Thermal Shock Resistance, points 20
21 to 22

Alloy Composition

Carbon (C), % 0
0.4 to 0.47
Iron (Fe), % 99.876 to 100
98.4 to 98.9
Manganese (Mn), % 0
0.7 to 1.0
Nitrogen (N), % 0 to 0.014
0
Phosphorus (P), % 0 to 0.055
0 to 0.040
Sulfur (S), % 0 to 0.055
0 to 0.050