EN 1.0060 Steel vs. SAE-AISI A4 Steel

Both EN 1.0060 steel and SAE-AISI A4 steel are iron alloys. They have a moderately high 94% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.0060 steel and the bottom bar is SAE-AISI A4 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 630
710 to 2050

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Melting Completion (Liquidus), °C 1470
1450
Melting Onset (Solidus), °C 1430
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 53
40
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.8
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 7.8
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 1.7
3.9
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.8
Embodied Energy, MJ/kg 18
24
Embodied Water, L/kg 45
59

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 22
25 to 73
Strength to Weight: Bending, points 21
23 to 46
Thermal Diffusivity, mm2/s 14
11
Thermal Shock Resistance, points 20
23 to 67

Alloy Composition

Carbon (C), % 0
1.0 to 1.1
Chromium (Cr), % 0
0.9 to 2.2
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 99.876 to 100
92 to 95.5
Manganese (Mn), % 0
1.8 to 2.2
Molybdenum (Mo), % 0
0.9 to 1.4
Nickel (Ni), % 0
0 to 0.3
Nitrogen (N), % 0 to 0.014
0
Phosphorus (P), % 0 to 0.055
0 to 0.030
Silicon (Si), % 0
0 to 0.5
Sulfur (S), % 0 to 0.055
0 to 0.030