EN 1.0060 Steel vs. N08926 Stainless Steel

Both EN 1.0060 steel and N08926 stainless steel are iron alloys. They have 46% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.0060 steel and the bottom bar is N08926 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 13
40
Fatigue Strength, MPa 200
290
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
80
Shear Strength, MPa 380
500
Tensile Strength: Ultimate (UTS), MPa 630
740
Tensile Strength: Yield (Proof), MPa 310
330

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 400
1100
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1410
Specific Heat Capacity, J/kg-K 470
460
Thermal Conductivity, W/m-K 53
12
Thermal Expansion, µm/m-K 12
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.8
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 7.8
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 1.7
33
Density, g/cm3 7.9
8.1
Embodied Carbon, kg CO2/kg material 1.4
6.2
Embodied Energy, MJ/kg 18
84
Embodied Water, L/kg 45
200

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 70
240
Resilience: Unit (Modulus of Resilience), kJ/m3 250
270
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 22
25
Strength to Weight: Bending, points 21
22
Thermal Diffusivity, mm2/s 14
3.2
Thermal Shock Resistance, points 20
16

Alloy Composition

Carbon (C), % 0
0 to 0.020
Chromium (Cr), % 0
19 to 21
Copper (Cu), % 0
0.5 to 1.5
Iron (Fe), % 99.876 to 100
41.7 to 50.4
Manganese (Mn), % 0
0 to 2.0
Molybdenum (Mo), % 0
6.0 to 7.0
Nickel (Ni), % 0
24 to 26
Nitrogen (N), % 0 to 0.014
0.15 to 0.25
Phosphorus (P), % 0 to 0.055
0 to 0.030
Silicon (Si), % 0
0 to 0.5
Sulfur (S), % 0 to 0.055
0 to 0.010