EN 1.0060 Steel vs. R30035 Cobalt

EN 1.0060 steel belongs to the iron alloys classification, while R30035 cobalt belongs to the cobalt alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.0060 steel and the bottom bar is R30035 cobalt.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
220 to 230
Elongation at Break, % 13
9.0 to 46
Fatigue Strength, MPa 200
170 to 740
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
84 to 89
Tensile Strength: Ultimate (UTS), MPa 630
900 to 1900
Tensile Strength: Yield (Proof), MPa 310
300 to 1650

Thermal Properties

Latent Heat of Fusion, J/g 250
320
Melting Completion (Liquidus), °C 1470
1440
Melting Onset (Solidus), °C 1430
1320
Specific Heat Capacity, J/kg-K 470
440
Thermal Conductivity, W/m-K 53
11
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.8
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 7.8
1.8

Otherwise Unclassified Properties

Base Metal Price, % relative 1.7
100
Density, g/cm3 7.9
8.7
Embodied Carbon, kg CO2/kg material 1.4
10
Embodied Energy, MJ/kg 18
140
Embodied Water, L/kg 45
410

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 70
160 to 320
Resilience: Unit (Modulus of Resilience), kJ/m3 250
210 to 5920
Stiffness to Weight: Axial, points 13
14 to 15
Stiffness to Weight: Bending, points 24
23 to 24
Strength to Weight: Axial, points 22
29 to 61
Strength to Weight: Bending, points 21
24 to 39
Thermal Diffusivity, mm2/s 14
3.0
Thermal Shock Resistance, points 20
23 to 46

Alloy Composition

Boron (B), % 0
0 to 0.015
Carbon (C), % 0
0 to 0.025
Chromium (Cr), % 0
19 to 21
Cobalt (Co), % 0
29.1 to 39
Iron (Fe), % 99.876 to 100
0 to 1.0
Manganese (Mn), % 0
0 to 0.15
Molybdenum (Mo), % 0
9.0 to 10.5
Nickel (Ni), % 0
33 to 37
Nitrogen (N), % 0 to 0.014
0
Phosphorus (P), % 0 to 0.055
0 to 0.015
Silicon (Si), % 0
0 to 0.15
Sulfur (S), % 0 to 0.055
0 to 0.010
Titanium (Ti), % 0
0 to 1.0