EN 1.0060 Steel vs. S35140 Stainless Steel

Both EN 1.0060 steel and S35140 stainless steel are iron alloys. They have 48% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.0060 steel and the bottom bar is S35140 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
210
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 13
34
Fatigue Strength, MPa 200
250
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
78
Shear Strength, MPa 380
460
Tensile Strength: Ultimate (UTS), MPa 630
690
Tensile Strength: Yield (Proof), MPa 310
310

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 400
1100
Melting Completion (Liquidus), °C 1470
1420
Melting Onset (Solidus), °C 1430
1370
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 53
14
Thermal Expansion, µm/m-K 12
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.8
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 7.8
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 1.7
31
Density, g/cm3 7.9
8.0
Embodied Carbon, kg CO2/kg material 1.4
5.5
Embodied Energy, MJ/kg 18
78
Embodied Water, L/kg 45
190

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 70
190
Resilience: Unit (Modulus of Resilience), kJ/m3 250
250
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 22
24
Strength to Weight: Bending, points 21
22
Thermal Diffusivity, mm2/s 14
3.7
Thermal Shock Resistance, points 20
16

Alloy Composition

Carbon (C), % 0
0 to 0.1
Chromium (Cr), % 0
20 to 22
Iron (Fe), % 99.876 to 100
44.1 to 52.7
Manganese (Mn), % 0
1.0 to 3.0
Molybdenum (Mo), % 0
1.0 to 2.0
Nickel (Ni), % 0
25 to 27
Niobium (Nb), % 0
0.25 to 0.75
Nitrogen (N), % 0 to 0.014
0.080 to 0.2
Phosphorus (P), % 0 to 0.055
0 to 0.045
Silicon (Si), % 0
0 to 0.75
Sulfur (S), % 0 to 0.055
0 to 0.030