EN 1.0213 Steel vs. EN 1.4971 Stainless Steel

Both EN 1.0213 steel and EN 1.4971 stainless steel are iron alloys. They have a modest 31% of their average alloy composition in common, which, by itself, doesn't mean much. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.0213 steel and the bottom bar is EN 1.4971 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 92 to 120
240
Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 12 to 25
34
Fatigue Strength, MPa 160 to 240
270
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
81
Shear Strength, MPa 230 to 270
530
Tensile Strength: Ultimate (UTS), MPa 320 to 430
800
Tensile Strength: Yield (Proof), MPa 220 to 330
340

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 400
1100
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1410
Specific Heat Capacity, J/kg-K 470
450
Thermal Conductivity, W/m-K 53
13
Thermal Expansion, µm/m-K 12
15

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
70
Density, g/cm3 7.9
8.4
Embodied Carbon, kg CO2/kg material 1.4
7.6
Embodied Energy, MJ/kg 18
110
Embodied Water, L/kg 46
300

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 33 to 98
220
Resilience: Unit (Modulus of Resilience), kJ/m3 120 to 300
280
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 11 to 15
26
Strength to Weight: Bending, points 13 to 16
23
Thermal Diffusivity, mm2/s 14
3.4
Thermal Shock Resistance, points 10 to 14
19

Alloy Composition

Aluminum (Al), % 0.020 to 0.060
0
Carbon (C), % 0.060 to 0.1
0.080 to 0.16
Chromium (Cr), % 0
20 to 22.5
Cobalt (Co), % 0
18.5 to 21
Iron (Fe), % 99.245 to 99.67
24.3 to 37.1
Manganese (Mn), % 0.25 to 0.45
0 to 2.0
Molybdenum (Mo), % 0
2.5 to 3.5
Nickel (Ni), % 0
19 to 21
Niobium (Nb), % 0
0.75 to 1.3
Nitrogen (N), % 0
0.1 to 0.2
Phosphorus (P), % 0 to 0.020
0 to 0.035
Silicon (Si), % 0 to 0.1
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.015
Tungsten (W), % 0
2.0 to 3.0