EN 1.0214 Steel vs. EN 1.6957 Steel

Both EN 1.0214 steel and EN 1.6957 steel are iron alloys. They have a moderately high 94% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.0214 steel and the bottom bar is EN 1.6957 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 97 to 130
280
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 12 to 31
18
Fatigue Strength, MPa 160 to 250
530
Poisson's Ratio 0.29
0.29
Reduction in Area, % 66 to 80
46
Shear Modulus, GPa 73
73
Shear Strength, MPa 250 to 290
570
Tensile Strength: Ultimate (UTS), MPa 330 to 460
930
Tensile Strength: Yield (Proof), MPa 210 to 360
780

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
450
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 53
47
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.9
7.9
Electrical Conductivity: Equal Weight (Specific), % IACS 7.9
9.1

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
5.0
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 1.4
2.1
Embodied Energy, MJ/kg 18
29
Embodied Water, L/kg 46
60

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 34 to 130
160
Resilience: Unit (Modulus of Resilience), kJ/m3 120 to 340
1630
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 12 to 16
33
Strength to Weight: Bending, points 14 to 17
27
Thermal Diffusivity, mm2/s 14
13
Thermal Shock Resistance, points 11 to 14
27

Alloy Composition

Aluminum (Al), % 0.020 to 0.060
0
Carbon (C), % 0.080 to 0.12
0.22 to 0.32
Chromium (Cr), % 0
1.2 to 1.8
Iron (Fe), % 99.17 to 99.6
92.7 to 94.7
Manganese (Mn), % 0.3 to 0.5
0.15 to 0.4
Molybdenum (Mo), % 0
0.25 to 0.45
Nickel (Ni), % 0
3.4 to 4.0
Phosphorus (P), % 0 to 0.025
0 to 0.010
Silicon (Si), % 0 to 0.1
0 to 0.15
Sulfur (S), % 0 to 0.025
0 to 0.0070
Vanadium (V), % 0
0.050 to 0.15