EN 1.0220 Steel vs. ACI-ASTM CE8MN Steel

Both EN 1.0220 steel and ACI-ASTM CE8MN steel are iron alloys. They have 62% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.0220 steel and the bottom bar is ACI-ASTM CE8MN steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 23
29
Fatigue Strength, MPa 210
370
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
80
Tensile Strength: Ultimate (UTS), MPa 390
750
Tensile Strength: Yield (Proof), MPa 290
500

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 400
1100
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 51
16
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
21
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.4
4.2
Embodied Energy, MJ/kg 18
58
Embodied Water, L/kg 46
180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 80
190
Resilience: Unit (Modulus of Resilience), kJ/m3 230
620
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 14
27
Strength to Weight: Bending, points 15
23
Thermal Diffusivity, mm2/s 14
4.2
Thermal Shock Resistance, points 12
21

Alloy Composition

Carbon (C), % 0 to 0.16
0 to 0.080
Chromium (Cr), % 0
22.5 to 25.5
Iron (Fe), % 98.2 to 100
56 to 66.4
Manganese (Mn), % 0 to 1.2
0 to 1.0
Molybdenum (Mo), % 0
3.0 to 4.5
Nickel (Ni), % 0
8.0 to 11
Nitrogen (N), % 0
0.1 to 0.3
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 0.35
0 to 1.5
Sulfur (S), % 0 to 0.045
0 to 0.040