EN 1.0220 Steel vs. AWS E308LMo

Both EN 1.0220 steel and AWS E308LMo are iron alloys. They have 66% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.0220 steel and the bottom bar is AWS E308LMo.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 23
40
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
78
Tensile Strength: Ultimate (UTS), MPa 390
580

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
16
Thermal Expansion, µm/m-K 12
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
19
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 1.4
3.8
Embodied Energy, MJ/kg 18
53
Embodied Water, L/kg 46
160

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 14
21
Strength to Weight: Bending, points 15
20
Thermal Diffusivity, mm2/s 14
4.2
Thermal Shock Resistance, points 12
15

Alloy Composition

Carbon (C), % 0 to 0.16
0 to 0.040
Chromium (Cr), % 0
18 to 21
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 98.2 to 100
59.6 to 70.5
Manganese (Mn), % 0 to 1.2
0.5 to 2.5
Molybdenum (Mo), % 0
2.0 to 3.0
Nickel (Ni), % 0
9.0 to 12
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.045
0 to 0.030