EN 1.0220 Steel vs. EN 1.4905 Stainless Steel

Both EN 1.0220 steel and EN 1.4905 stainless steel are iron alloys. They have 88% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.0220 steel and the bottom bar is EN 1.4905 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
19
Fatigue Strength, MPa 210
330
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Shear Strength, MPa 250
460
Tensile Strength: Ultimate (UTS), MPa 390
740
Tensile Strength: Yield (Proof), MPa 290
510

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Maximum Temperature: Mechanical, °C 400
660
Melting Completion (Liquidus), °C 1460
1480
Melting Onset (Solidus), °C 1420
1440
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
26
Thermal Expansion, µm/m-K 12
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
3.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
4.2

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
9.5
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 1.4
2.8
Embodied Energy, MJ/kg 18
40
Embodied Water, L/kg 46
90

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 80
130
Resilience: Unit (Modulus of Resilience), kJ/m3 230
680
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 14
26
Strength to Weight: Bending, points 15
23
Thermal Diffusivity, mm2/s 14
7.0
Thermal Shock Resistance, points 12
25

Alloy Composition

Aluminum (Al), % 0
0 to 0.040
Boron (B), % 0
0.00050 to 0.0050
Carbon (C), % 0 to 0.16
0.090 to 0.13
Chromium (Cr), % 0
8.5 to 9.5
Iron (Fe), % 98.2 to 100
86.2 to 88.8
Manganese (Mn), % 0 to 1.2
0.3 to 0.6
Molybdenum (Mo), % 0
0.9 to 1.1
Nickel (Ni), % 0
0.1 to 0.4
Niobium (Nb), % 0
0.060 to 0.1
Nitrogen (N), % 0
0.050 to 0.090
Phosphorus (P), % 0 to 0.045
0 to 0.020
Silicon (Si), % 0 to 0.35
0.1 to 0.5
Sulfur (S), % 0 to 0.045
0 to 0.010
Tungsten (W), % 0
0.9 to 1.1
Vanadium (V), % 0
0.18 to 0.25