EN 1.0220 Steel vs. SAE-AISI 1108 Steel

Both EN 1.0220 steel and SAE-AISI 1108 steel are iron alloys. Their average alloy composition is basically identical. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.0220 steel and the bottom bar is SAE-AISI 1108 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 110
110 to 140
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
23 to 34
Fatigue Strength, MPa 210
170 to 260
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 250
250 to 280
Tensile Strength: Ultimate (UTS), MPa 390
380 to 440
Tensile Strength: Yield (Proof), MPa 290
220 to 360

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
52
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
1.8
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 18
18
Embodied Water, L/kg 46
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 80
95 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 230
130 to 340
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 14
13 to 16
Strength to Weight: Bending, points 15
15 to 16
Thermal Diffusivity, mm2/s 14
14
Thermal Shock Resistance, points 12
12 to 14

Alloy Composition

Carbon (C), % 0 to 0.16
0.080 to 0.13
Iron (Fe), % 98.2 to 100
98.9 to 99.24
Manganese (Mn), % 0 to 1.2
0.6 to 0.8
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 0.35
0
Sulfur (S), % 0 to 0.045
0.080 to 0.13