EN 1.0258 Steel vs. 5088 Aluminum

EN 1.0258 steel belongs to the iron alloys classification, while 5088 aluminum belongs to the aluminum alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN 1.0258 steel and the bottom bar is 5088 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
68
Elongation at Break, % 23
29
Fatigue Strength, MPa 200
180
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 73
25
Shear Strength, MPa 310
200
Tensile Strength: Ultimate (UTS), MPa 490
310
Tensile Strength: Yield (Proof), MPa 290
150

Thermal Properties

Latent Heat of Fusion, J/g 250
390
Maximum Temperature: Mechanical, °C 400
200
Melting Completion (Liquidus), °C 1460
640
Melting Onset (Solidus), °C 1420
540
Specific Heat Capacity, J/kg-K 470
900
Thermal Conductivity, W/m-K 49
120
Thermal Expansion, µm/m-K 12
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
29
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
98

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
9.5
Density, g/cm3 7.9
2.7
Embodied Carbon, kg CO2/kg material 1.5
9.0
Embodied Energy, MJ/kg 19
150
Embodied Water, L/kg 47
1180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 95
76
Resilience: Unit (Modulus of Resilience), kJ/m3 220
170
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
50
Strength to Weight: Axial, points 17
32
Strength to Weight: Bending, points 18
38
Thermal Diffusivity, mm2/s 13
51
Thermal Shock Resistance, points 16
14

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
92.4 to 94.8
Carbon (C), % 0 to 0.2
0
Chromium (Cr), % 0 to 0.3
0 to 0.15
Copper (Cu), % 0 to 0.3
0 to 0.25
Iron (Fe), % 96.9 to 100
0.1 to 0.35
Magnesium (Mg), % 0
4.7 to 5.5
Manganese (Mn), % 0 to 1.4
0.2 to 0.5
Molybdenum (Mo), % 0 to 0.080
0
Nickel (Ni), % 0 to 0.3
0
Niobium (Nb), % 0 to 0.010
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.4
0 to 0.2
Sulfur (S), % 0 to 0.020
0
Titanium (Ti), % 0 to 0.040
0
Vanadium (V), % 0 to 0.020
0
Zinc (Zn), % 0
0.2 to 0.4
Zirconium (Zr), % 0
0 to 0.15
Residuals, % 0
0 to 0.15