EN 1.0258 Steel vs. 6182 Aluminum

EN 1.0258 steel belongs to the iron alloys classification, while 6182 aluminum belongs to the aluminum alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN 1.0258 steel and the bottom bar is 6182 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
70
Elongation at Break, % 23
6.8 to 13
Fatigue Strength, MPa 200
63 to 99
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 73
26
Shear Strength, MPa 310
140 to 190
Tensile Strength: Ultimate (UTS), MPa 490
230 to 320
Tensile Strength: Yield (Proof), MPa 290
130 to 270

Thermal Properties

Latent Heat of Fusion, J/g 250
410
Maximum Temperature: Mechanical, °C 400
190
Melting Completion (Liquidus), °C 1460
640
Melting Onset (Solidus), °C 1420
600
Specific Heat Capacity, J/kg-K 470
900
Thermal Conductivity, W/m-K 49
160
Thermal Expansion, µm/m-K 12
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
40
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
130

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
9.5
Density, g/cm3 7.9
2.7
Embodied Carbon, kg CO2/kg material 1.5
8.4
Embodied Energy, MJ/kg 19
150
Embodied Water, L/kg 47
1170

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 95
21 to 26
Resilience: Unit (Modulus of Resilience), kJ/m3 220
110 to 520
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
50
Strength to Weight: Axial, points 17
23 to 32
Strength to Weight: Bending, points 18
30 to 38
Thermal Diffusivity, mm2/s 13
65
Thermal Shock Resistance, points 16
10 to 14

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
95 to 97.9
Carbon (C), % 0 to 0.2
0
Chromium (Cr), % 0 to 0.3
0 to 0.25
Copper (Cu), % 0 to 0.3
0 to 0.1
Iron (Fe), % 96.9 to 100
0 to 0.5
Magnesium (Mg), % 0
0.7 to 1.2
Manganese (Mn), % 0 to 1.4
0.5 to 1.0
Molybdenum (Mo), % 0 to 0.080
0
Nickel (Ni), % 0 to 0.3
0
Niobium (Nb), % 0 to 0.010
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.4
0.9 to 1.3
Sulfur (S), % 0 to 0.020
0
Titanium (Ti), % 0 to 0.040
0 to 0.1
Vanadium (V), % 0 to 0.020
0
Zinc (Zn), % 0
0 to 0.2
Zirconium (Zr), % 0
0.050 to 0.2
Residuals, % 0
0 to 0.15