EN 1.0258 Steel vs. ACI-ASTM CF3 Steel

Both EN 1.0258 steel and ACI-ASTM CF3 steel are iron alloys. They have 70% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.0258 steel and the bottom bar is ACI-ASTM CF3 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
140
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 23
60
Fatigue Strength, MPa 200
270
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Tensile Strength: Ultimate (UTS), MPa 490
510
Tensile Strength: Yield (Proof), MPa 290
250

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 400
960
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1420
1450
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 49
16
Thermal Expansion, µm/m-K 12
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
16
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.5
3.2
Embodied Energy, MJ/kg 19
45
Embodied Water, L/kg 47
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 95
250
Resilience: Unit (Modulus of Resilience), kJ/m3 220
160
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 17
18
Strength to Weight: Bending, points 18
18
Thermal Diffusivity, mm2/s 13
4.3
Thermal Shock Resistance, points 16
11

Alloy Composition

Carbon (C), % 0 to 0.2
0 to 0.030
Chromium (Cr), % 0 to 0.3
17 to 21
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 96.9 to 100
62.9 to 75
Manganese (Mn), % 0 to 1.4
0 to 1.5
Molybdenum (Mo), % 0 to 0.080
0 to 0.5
Nickel (Ni), % 0 to 0.3
8.0 to 12
Niobium (Nb), % 0 to 0.010
0
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.4
0 to 2.0
Sulfur (S), % 0 to 0.020
0 to 0.040
Titanium (Ti), % 0 to 0.040
0
Vanadium (V), % 0 to 0.020
0