EN 1.0258 Steel vs. EN 1.0050 Steel

Both EN 1.0258 steel and EN 1.0050 steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.0258 steel and the bottom bar is EN 1.0050 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
150
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
18
Fatigue Strength, MPa 200
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 310
330
Tensile Strength: Ultimate (UTS), MPa 490
530
Tensile Strength: Yield (Proof), MPa 290
280

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1470
Melting Onset (Solidus), °C 1420
1430
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 49
53
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
6.8
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
7.8

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
1.7
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 1.5
1.4
Embodied Energy, MJ/kg 19
18
Embodied Water, L/kg 47
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 95
81
Resilience: Unit (Modulus of Resilience), kJ/m3 220
210
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17
19
Strength to Weight: Bending, points 18
18
Thermal Diffusivity, mm2/s 13
14
Thermal Shock Resistance, points 16
17

Alloy Composition

Carbon (C), % 0 to 0.2
0
Chromium (Cr), % 0 to 0.3
0
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 96.9 to 100
99.876 to 100
Manganese (Mn), % 0 to 1.4
0
Molybdenum (Mo), % 0 to 0.080
0
Nickel (Ni), % 0 to 0.3
0
Niobium (Nb), % 0 to 0.010
0
Nitrogen (N), % 0
0 to 0.014
Phosphorus (P), % 0 to 0.025
0 to 0.055
Silicon (Si), % 0 to 0.4
0
Sulfur (S), % 0 to 0.020
0 to 0.055
Titanium (Ti), % 0 to 0.040
0
Vanadium (V), % 0 to 0.020
0