EN 1.0258 Steel vs. S82031 Stainless Steel

Both EN 1.0258 steel and S82031 stainless steel are iron alloys. They have 75% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.0258 steel and the bottom bar is S82031 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 23
39
Fatigue Strength, MPa 200
490
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
78
Shear Strength, MPa 310
540
Tensile Strength: Ultimate (UTS), MPa 490
780
Tensile Strength: Yield (Proof), MPa 290
570

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 400
980
Melting Completion (Liquidus), °C 1460
1430
Melting Onset (Solidus), °C 1420
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 49
15
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
13
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 1.5
2.8
Embodied Energy, MJ/kg 19
39
Embodied Water, L/kg 47
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 95
280
Resilience: Unit (Modulus of Resilience), kJ/m3 220
820
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 17
28
Strength to Weight: Bending, points 18
24
Thermal Diffusivity, mm2/s 13
3.9
Thermal Shock Resistance, points 16
22

Alloy Composition

Carbon (C), % 0 to 0.2
0 to 0.050
Chromium (Cr), % 0 to 0.3
19 to 22
Copper (Cu), % 0 to 0.3
0 to 1.0
Iron (Fe), % 96.9 to 100
68 to 78.3
Manganese (Mn), % 0 to 1.4
0 to 2.5
Molybdenum (Mo), % 0 to 0.080
0.6 to 1.4
Nickel (Ni), % 0 to 0.3
2.0 to 4.0
Niobium (Nb), % 0 to 0.010
0
Nitrogen (N), % 0
0.14 to 0.24
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.4
0 to 0.8
Sulfur (S), % 0 to 0.020
0 to 0.0050
Titanium (Ti), % 0 to 0.040
0
Vanadium (V), % 0 to 0.020
0