EN 1.0258 Steel vs. ZA-8

EN 1.0258 steel belongs to the iron alloys classification, while ZA-8 belongs to the zinc alloys. There are 31 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.0258 steel and the bottom bar is ZA-8.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
87 to 100
Elastic (Young's, Tensile) Modulus, GPa 190
85 to 86
Elongation at Break, % 23
1.3 to 8.0
Fatigue Strength, MPa 200
51 to 100
Poisson's Ratio 0.29
0.26
Shear Modulus, GPa 73
34
Shear Strength, MPa 310
240 to 280
Tensile Strength: Ultimate (UTS), MPa 490
210 to 370
Tensile Strength: Yield (Proof), MPa 290
210 to 290

Thermal Properties

Latent Heat of Fusion, J/g 250
110
Maximum Temperature: Mechanical, °C 400
100
Melting Completion (Liquidus), °C 1460
400
Melting Onset (Solidus), °C 1420
380
Specific Heat Capacity, J/kg-K 470
440
Thermal Conductivity, W/m-K 49
120
Thermal Expansion, µm/m-K 12
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
28
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
40

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
11
Density, g/cm3 7.9
6.3
Embodied Carbon, kg CO2/kg material 1.5
3.3
Embodied Energy, MJ/kg 19
62
Embodied Water, L/kg 47
420

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 95
2.8 to 28
Resilience: Unit (Modulus of Resilience), kJ/m3 220
260 to 490
Stiffness to Weight: Axial, points 13
7.5
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 17
9.3 to 17
Strength to Weight: Bending, points 18
12 to 18
Thermal Diffusivity, mm2/s 13
42
Thermal Shock Resistance, points 16
7.6 to 13

Alloy Composition

Aluminum (Al), % 0
8.0 to 8.8
Cadmium (Cd), % 0
0 to 0.0060
Carbon (C), % 0 to 0.2
0
Chromium (Cr), % 0 to 0.3
0
Copper (Cu), % 0 to 0.3
0.8 to 1.3
Iron (Fe), % 96.9 to 100
0 to 0.075
Lead (Pb), % 0
0 to 0.0060
Magnesium (Mg), % 0
0.015 to 0.030
Manganese (Mn), % 0 to 1.4
0
Molybdenum (Mo), % 0 to 0.080
0
Nickel (Ni), % 0 to 0.3
0 to 0.020
Niobium (Nb), % 0 to 0.010
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.4
0 to 0.045
Sulfur (S), % 0 to 0.020
0
Tin (Sn), % 0
0 to 0.0030
Titanium (Ti), % 0 to 0.040
0
Vanadium (V), % 0 to 0.020
0
Zinc (Zn), % 0
89.7 to 91.2