EN 1.0259 (P265TR2) Non-Alloy Steel
EN 1.0259 steel is a carbon (non-alloy) steel formulated for primary forming into wrought products. Cited properties are appropriate for the normalized condition. 1.0259 is the EN numeric designation for this material. P265TR2 is the EN chemical designation.
It has a moderately high electrical conductivity and a moderately low thermal conductivity among wrought carbon or non-alloy steels.
The graph bars on the material properties cards below compare EN 1.0259 steel to: wrought carbon or non-alloy steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
140
Elastic (Young's, Tensile) Modulus
190 GPa 27 x 106 psi
Elongation at Break
23 %
Fatigue Strength
200 MPa 29 x 103 psi
Impact Strength: V-Notched Charpy
38 J 28 ft-lb
Poisson's Ratio
0.29
Shear Modulus
73 GPa 11 x 106 psi
Shear Strength
310 MPa 45 x 103 psi
Tensile Strength: Ultimate (UTS)
490 MPa 71 x 103 psi
Tensile Strength: Yield (Proof)
280 MPa 41 x 103 psi
Thermal Properties
Latent Heat of Fusion
250 J/g
Maximum Temperature: Mechanical
400 °C 750 °F
Melting Completion (Liquidus)
1460 °C 2660 °F
Melting Onset (Solidus)
1420 °C 2590 °F
Specific Heat Capacity
470 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
49 W/m-K 28 BTU/h-ft-°F
Thermal Expansion
12 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
7.3 % IACS
Electrical Conductivity: Equal Weight (Specific)
8.4 % IACS
Otherwise Unclassified Properties
Base Metal Price
2.1 % relative
Density
7.8 g/cm3 490 lb/ft3
Embodied Carbon
1.5 kg CO2/kg material
Embodied Energy
19 MJ/kg 8.4 x 103 BTU/lb
Embodied Water
49 L/kg 5.8 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
95 MJ/m3
Resilience: Unit (Modulus of Resilience)
210 kJ/m3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
17 points
Strength to Weight: Bending
18 points
Thermal Diffusivity
13 mm2/s
Thermal Shock Resistance
15 points
Alloy Composition
| Fe | 96.7 to 99.98 | |
| Mn | 0 to 1.4 | |
| Si | 0 to 0.4 | |
| Cr | 0 to 0.3 | |
| Ni | 0 to 0.3 | |
| Cu | 0 to 0.3 | |
| Al | 0.020 to 0.2 | |
| C | 0 to 0.2 | |
| Mo | 0 to 0.080 | |
| Ti | 0 to 0.040 | |
| P | 0 to 0.025 | |
| V | 0 to 0.020 | |
| S | 0 to 0.015 | |
| Nb | 0 to 0.010 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Similar Alloys
Further Reading
EN 10216-1: Seamless steel tubes for pressure purposes - Technical delivery conditions - Part 1: Non-alloy steel tubes with specified room temperature properties
EN 10217-1: Welded steel tubes for pressure purposes - Technical delivery conditions - Part 1: Non-alloy steel tubes with specified room temperature properties
Microstructure of Steels and Cast Irons, Madeleine Durand-Charre, 2004
Carbon Steel Handbook, D. Gandy, 2007
Ferrous Materials: Steel and Cast Iron, Hans Berns and Werner Theisen, 2008
CRC Materials Science and Engineering Handbook, 4th ed., James F. Shackelford et al. (editors), 2015
Steels: Processing, Structure, and Performance, 2nd ed., George Krauss, 2015