EN 1.0303 Steel vs. ASTM A372 Grade M Steel

Both EN 1.0303 steel and ASTM A372 grade M steel are iron alloys. They have a moderately high 94% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.0303 steel and the bottom bar is ASTM A372 grade M steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 84 to 120
240 to 280
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 12 to 25
18 to 21
Fatigue Strength, MPa 150 to 230
450 to 520
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 220 to 260
510 to 570
Tensile Strength: Ultimate (UTS), MPa 290 to 410
810 to 910
Tensile Strength: Yield (Proof), MPa 200 to 320
660 to 770

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
450
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 53
46
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.9
8.0
Electrical Conductivity: Equal Weight (Specific), % IACS 7.9
9.1

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
5.0
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 1.4
2.0
Embodied Energy, MJ/kg 18
27
Embodied Water, L/kg 46
61

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 30 to 94
160
Resilience: Unit (Modulus of Resilience), kJ/m3 110 to 270
1140 to 1580
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 10 to 15
29 to 32
Strength to Weight: Bending, points 12 to 16
24 to 27
Thermal Diffusivity, mm2/s 14
12
Thermal Shock Resistance, points 9.2 to 13
24 to 27

Alloy Composition

Aluminum (Al), % 0.020 to 0.060
0
Carbon (C), % 0.020 to 0.060
0 to 0.23
Chromium (Cr), % 0
1.5 to 2.0
Iron (Fe), % 99.335 to 99.71
92.5 to 95.1
Manganese (Mn), % 0.25 to 0.4
0.2 to 0.4
Molybdenum (Mo), % 0
0.4 to 0.6
Nickel (Ni), % 0
2.8 to 3.9
Phosphorus (P), % 0 to 0.020
0 to 0.015
Silicon (Si), % 0 to 0.1
0 to 0.3
Sulfur (S), % 0 to 0.025
0 to 0.010
Vanadium (V), % 0
0 to 0.080

Comparable Variants