EN 1.0345 Steel vs. EN 1.0481 Steel

Both EN 1.0345 steel and EN 1.0481 steel are iron alloys. Both are furnished in the normalized condition. Their average alloy composition is basically identical.

For each property being compared, the top bar is EN 1.0345 steel and the bottom bar is EN 1.0481 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 120
150
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 27
24
Fatigue Strength, MPa 170
210
Impact Strength: V-Notched Charpy, J 44
46
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 270
330
Tensile Strength: Ultimate (UTS), MPa 420
510
Tensile Strength: Yield (Proof), MPa 230
300

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 49
50
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
2.2
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.5
1.5
Embodied Energy, MJ/kg 19
20
Embodied Water, L/kg 48
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 96
100
Resilience: Unit (Modulus of Resilience), kJ/m3 140
230
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 15
18
Strength to Weight: Bending, points 16
18
Thermal Diffusivity, mm2/s 13
13
Thermal Shock Resistance, points 13
16

Alloy Composition

Aluminum (Al), % 0.020 to 0.024
0.020 to 0.024
Carbon (C), % 0 to 0.16
0.080 to 0.2
Chromium (Cr), % 0 to 0.3
0 to 0.3
Copper (Cu), % 0 to 0.3
0 to 0.3
Iron (Fe), % 97.2 to 99.38
96.8 to 99
Manganese (Mn), % 0.6 to 1.2
0.9 to 1.5
Molybdenum (Mo), % 0 to 0.080
0 to 0.080
Nickel (Ni), % 0 to 0.3
0 to 0.3
Niobium (Nb), % 0 to 0.020
0 to 0.020
Nitrogen (N), % 0 to 0.012
0 to 0.012
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0 to 0.35
0 to 0.4
Sulfur (S), % 0 to 0.010
0 to 0.010
Titanium (Ti), % 0 to 0.030
0 to 0.030
Vanadium (V), % 0 to 0.020
0 to 0.020